Constituents   Percentage
    %
Aluminium Oxide Al2O3 28.70
Ferric Oxide Fe2O3 1.40
Titanium Oxide TiO2 .085
Calcium Oxide CaO 0.18
Magnesium Oxide MgO 0.02
Silica SiO2 57.88
Loss on Ignition L.O.I. 10.59
 
Crude China Clay White Test Report
 
Constituents   Percentage
    %
Silica SiO2 47.50
Alumina Al2O3 36.02
Ferric Oxide Fe2O3 0.58
Titanium Dioxide TiO2 1.38
Mangenous Oxide MnO Nil
Calcium Oxide CaO Nil
Magnesium Oxide MgO 0.79
Sodium Oxide Na2O 0.71
Potassium Oxide K2O 0.20
Loss on Ignition L.O.I. 12.81
 
Crude China Clay Test Report
 
Constituents   Percentage
    %
Silica SiO2 54.88
Alumina Al2O3 30.15
Ferric Oxide Fe2O3 0.58
Titanium Dioxide TiO2 1.52
Maganous Oxide MnO Nil
Calcium Oxide CaO Nil
Magnesium Oxide MgO 1.09
Sodium Oxide Na2O 0.91
Potassium Oxide KO 0.64
Loss on Ignition L.O.I. 10.23
 
Levigated China Clay Test Report
 
Constituents   Percentage
    %
Alumina as Al2O3 % IS 2840 2002 34.61
Calcium as CaO % IS 5949 1990 (Reaff 2003) 0.39
Iron as Fe2O3 % IS 2840 2002 0.86
Loss on Igniton (L.O.I.) % IS 2840 2002 12.53
Magnesium as MgO % IS 5949 1990 (Reaff 2003) 0.03
Moisture Content % IS 7589 1974 (Reaff Firm ED 1998) 3.57
Potassium as K2O % IS 9749 1981 (reaff Firm ED 1990) 0.40
Silica as SiO2 % IS 2840 2002 48.81
Sodium as Na2O % IS 9749 1981 (reaff Firm ED 1990) 0.28
Titanium as TiO2 % IS 2840 2002 1.64
Water of Plasticity % IS 2840 1993 35.50
 
Kaolin Powder Clay Test Report
 
 
Constituents   Percentage
    %
Aluminum Oxide as Al2O3 IS 9749 1981 (Reaff 1990) 32.04%
Calcium (as CaO ) IS 5949 1990 (Reaff 1995) 0.17%
Iron Oxide as Fe2O3 IS 9749 1981 (Reaff 1990) 0.71%
Loss on Drying IS 7589 1974 0.42%
Loss on Igniti0n (at 1000OC) IS 9749 1981 (Reaff 1990) 11.91%
Magnesium (as MgO) IS 5949 1990 (Reaff 1995) 0.07%
Potassium (as K2O) IS 9497 1980 (Reaff 1998) 0.16%
Silica IS 9749 1981 (Reaff 1990) 52.73%
Sodium (as Na2O ) IS 9497 1980 (Reaff 1998) 0.15%
Titanium Di-Oxide (as TiO2) IS 1917 PART 7 2001 1.70%
Water of Plasticity IS 2840 2002 32.76%
Chaina Clay